Sikasil®-129 Kitchen & Bathroom
SILICONE SEALANT FOR KITCHEN AND BATHROOM
Sikasil®-129 Kitchen & Bathroom is a 1-component silicone sealant with resistance to fungus. Suitable for hot and tropical climate conditions.
- Long term fungus and mildew resistance
- Primerless adhesion to a wide range of substrates
- High elasticity and flexibility
- Low odor, neutral curing
- Non-corrosive
- Solvent-free
- Very good UV and weathering resistance
Usage
Sikasil®-129 Kitchen & Bathroom is designed for sanitary and other sealing applications in wet room where mildew resistance is required.- Wet areas
- Internal and external
- Multi substrate: metal (not including copper), glass, stone, aluminium, plastic, ceramic and porcelain
Advantages
- Long term fungus and mildew resistance
- Primerless adhesion to a wide range of substrates
- High elasticity and flexibility
- Low odor, neutral curing
- Non-corrosive
- Solvent-free
- Very good UV and weathering resistance
Packaging
300 ml cartridge
Colour
- Black
- White
- Grey
- others on request
Product Details
Chemical Base
Neutral curing silicone
Shelf Life
12 months from the date of production, if it is stored in undamaged, original, sealed packaging, and if the storage conditions are met.
Storage Conditions
Stored in cool and dry conditions, where it is protected from direct sunlight and at temperatures below +27 °C.
Density
~1.45–1.55 g/cm³ | (ISO 868) at +23 ± 2 °C, 50 % r.h |
Shore A Hardness
30–50 | (ISO 868) |
Tensile Strength
~1 MPa | (ISO 8339) |
Movement Capability
25 % | (ASTM C719) |
Elastic Recovery
80 % | (ISO 7389) |
Joint Design
The joint width must be designed to be within the movement capability of the sealant. In general the joint width must be ≥ 6 mm and ≤ 20 mm. The width to depth ratio of ~2 : 1 must be respected.
For larger joints please contact our Technical Department.
Application
Extrusion rate
100–200 ml/min | (GB/T 13477) |
Sag Flow
≤ 1 mm | (ISO 7390) |
Ambient Air Temperature
+5 °C min. / +40 °C max.
Substrate Temperature
+5 °C min. / +40 °C max.
Curing Rate
3 mm / day (at +23 ± 2 °C, 50 % r.h)
Tack Free Time
~10–30 minutes | (CQP 019-1) at 23 °C / 50 % r.h. |
Consumption
Joint Width | Joint Depth | Joint Length / 300 ml |
6 mm | 4 mm | ~12.5 m |
9 mm | 5 mm | ~6.5 m |
12 mm | 6 mm | ~4 m |
20 mm | 10 mm | ~1.5 m |
SUBSTRATE PREPARATION
The substrate must be sound, clean, dry and free of all contaminants such as dirt, oil, grease, old sealants and poorly bonded paint coatings which could affect adhesion of the sealant. The substrate must be of sufficient strength to resist the stresses induced by the sealant during movement.
All dust, loose and friable material must be completely removed from all surfaces using suitable equipment before application of any activators, primers or sealant.
Sikasil®-129 Kitchen & Bathroom adheres without primers and/or activators.
For optimum adhesion, joint durability and critical, high performance applications such as joints on multi-storey buildings, highly stressed joints, extreme weather exposure or water immersion / exposure, the following priming and/or pre-treatment procedures must be followed:
Non-porous substrates
Aluminium, anodised aluminium, stainless steel, PVC, galvanised steel, powder coated metals or glazed tiles. Slightly roughen surface with a fine abrasive pad. Clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth.
Before sealing, allow a waiting time of > 15 minutes (< 6 hours).
Other metals, such as copper, brass and titanium-zinc, clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth. After a waiting time of > 15 minutes (< 6 hours), apply Sika® Primer-3 N by brush. Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
PVC has to be cleaned and pre-treated using Sika® Primer-215 applied with a brush. Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
Glass must be cleaned with Isopropanol before application.
Porous substrates
Porous substrates must be primed using Sika® Primer-3 N applied by brush.
Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
Adhesion tests on project specific substrates must be performed and procedures agreed with all parties before full project application.
For more detailed advice and instructions contact Sika Technical Services.
Note: Primers and activators are adhesion promoters and not an alternative to improve poor preparation / cleaning of the joint surface. Primers also improve the long term adhesion performance of the sealed joint.
CLEANING OF TOOLS
Clean all tools and application equipment with Sika® Remover-208 immediately after use. Hardened material can only be removed mechanically. For cleaning skin, use Sika® Cleaning Wipes-100.