S-Welding cord PVC
S-Welding cord PVC is made of PVC-P by extruding procedure.
- Hot air weldable
Usage
S-Welding cord PVC is used at perimeter fastening of mechanicially fastened flat roof systems and roof systems with ballast using Sarnabar to prevent the membrane from slipping.Advantages
- Hot air weldable
Packaging
Plastic pail
Colour
| Surface: | smooth |
| Colour: | red |
Product Details
Chemical Base
Polyvinyl Chloride (PVC-P) compound extruded
Shelf Life
5 years from date of production.
Storage Conditions
Product must be stored in original unopened and undamaged sealed packaging in dry conditions and temperatures between + 5 °C and + 30 °C. Always refer to packaging.
Length
100 m
Thickness
Diameter 4 mm (+/- 0.2 mm)
Mass per Unit Area
18 g/m (+/- 10 %)
System Structure
The following products must be considered for use depending on roof design:
- Leister tubular nozzle 5 mm
- Leister speed weld nozzle 4 mm
- Sarnafil® G 410-types
- Sarnafil® G 411-types
- Sarnafil® S 327-types
- Sikaplan® G / VG / VGWT / S / SG / SGmA
Compatibility
Not applicable for permanent exposure to UV irradiation.
Application
Ambient Air Temperature
- 20 °C min. / + 60 °C max.
Substrate Temperature
- 30 °C min. / + 60 °C max.
APPLICATION
According to the valid installation instructions for Sarnafil® G/S flat roof waterproofing membranes. Using the Leister tubular nozzle 5 mm and the Leister speed weld nozzle 4 mm of the Leister Triac PID. The S-Welding Cord PVC is welded to the membrane along the Sarnabar perimeter fastening to prevent the membrane from slipping.